High voltage EDLC cell and method for the manufacture thereof

ABSTRACT

A method of manufacturing an electrode includes printing an electrode ink on a portion of a substrate using a rotary lithographic printer. The electrode ink is allowed to dry on the substrate. A separator material is printed on the portion of the substrate using the rotary lithographic printer. A sealant wall is printed around the portion of the substrate using the rotary lithographic printer.

CROSS REFERENCE TO RELATED CASES

This application claims priority to and is a continuation of U.S. patentapplication Ser. No. 13/061,409, now U.S. Pat. No. 9,245,693, filed onMay 13, 2011, entitled “High Voltage EDLC Cell and Method for theManufacture Thereof,” which is a national stage entry ofPCT/US2009/055299, filed on Aug. 28, 2009, entitled “High Voltage EDLCCell and Method for the Manufacture Thereof,” which is acontinuation-in-part of U.S. patent application Ser. No. 12/229,922, nowU.S. Pat. No. 8,411,413, filed Aug. 28, 2008, entitled “High VoltageEDLC Cell and Method for the Manufacture Thereof,” each of which areincorporated herein by reference in their entirety. This application isalso related to U.S. patent application Ser. No. 12/151,811, filed May8, 2008, entitled “Electrode Structure for the Manufacture of anElectric Double Layer Capacitor,” which is incorporated herein byreference in its entirety.

BACKGROUND

The present invention relates to high voltage electrochemical doublelayer capacitors (EDLCs) and, more particularly, to a prototype design,manufacturing methods and materials to create electrodes for a highvoltage EDLC, while maintaining high capacitance and low resistancethereof.

An electrochemical double layer capacitor (EDLC) is an energy storagedevice consisting of two electrodes arranged in such a manner that oneacts as the cathode and the other the anode, creating a structure thatcan be modeled as two capacitors in series. The device is characterizedby a high power density whose value can be dictated by the effectiveseries resistance (ESR) of the device (i.e., the lower the ESR, thehigher the power density). The capacitance of EDLCs can be large due tothe effective surface of activated carbon used to fabricate an EDLCs andthe spacing between the electrode and the molecules of the electrolytethat form the double layers. The capacitance of an EDLC can becalculated using the formula C=kA/d, where k is a constant ofproportionality. A is the effective surface area of the activatedcarbon, and d is the spacing between the electrode and the electrolytemolecules.

EDLC devices can be manufactured by encasing electrodes and separatormaterial in a package which is wetted with electrolyte and sealed. Theresulting device is a single cell EDLC device. These devices can be usedin a wide variety of applications including but not limited toindustrial power supplies, UPS (uninterrupted power supplies), electricvehicles, cell phones, and electronic appliances.

Known EDLCs operate with a nominal voltage rating of approximately 2.7volts, a limitation imposed by virtue of the electrolyte. In someapplications, more than a single EDLC cell is required to meet, theneeds of a particular application. For example, one or more EDLC devicescan be coupled in series to provide a composite device that operates ata higher voltage. However, if the cells are not balanced as the numberof cells in series increases premature failure of the composite devicecan occur. Additionally, the increase of the ESR of the cells in seriescan result in a decrease power density.

SUMMARY

A method of manufacturing an electrode includes printing an electrodeink on a portion of a substrate using a rotary lithographic printer. Theelectrode ink is allowed to dry on the substrate. A separator materialis printed on the portion of the substrate using the rotary lithographicprinter. A sealant wall is printed around the portion of the substrateusing the rotary lithographic printer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the basic component shapes used in staging the variousareas of the electrodes, according to an embodiment.

FIG. 1A is a schematic illustration of a rotary lithographic printer,according to an embodiment.

FIGS. 1B-1D are schematic illustrations of various electrode arraysprinted using the rotary lithographic printer of FIG. 1A.

FIG. 1E is a flow chart illustrating a method of printing an electrode,according to an embodiment.

FIG. 2 shows a component selection and specific placement thereofaccording to an embodiment.

FIG. 3 illustrates the folding organization patterns used to completeeach cell sequentially, according to an embodiment.

FIG. 3A is a schematic illustration of three stacks of electrodesconnected in parallel, according to an embodiment.

FIG. 4 shows an open, view of one electrode, the component patternsbeing shown in sequence from front to back side, indicating how theyappear when folded, according to an embodiment.

FIG. 5 shows the block structure of the high voltage stack and theinterface components used, to stack the voltage into increments,according to embodiment.

FIG. 6 is a schematic view of the detailed high voltage EDLC, accordingto an embodiment.

FIG. 7 shows a high voltage EDLC structure, according to an embodiment.

FIG. 8 shows a thermal transfer material, being added into a highvoltage EDLC, according to an embodiment.

FIG. 9 is a schematic view of a final high voltage design packaging,according to an embodiment.

DETAILED DESCRIPTION

In some embodiments, a method of manufacturing an electrode includesprinting an electrode ink on a portion of a substrate using a rotarylithographic printer. The electrode ink is allowed to dry on thesubstrate. A separator material is printed on the portion of thesubstrate using the rotary lithographic printer. A sealant wall isprinted amend the portion of the substrate using the rotary lithographicprinter.

In some embodiments, a rotary lithographic printer can include a firstrotating drum and a second rotating drum. A mesh is coupled to the firstrotating drum. The electrode ink can be configured to be pressed ontothe portion of the substrate through the mesh by the first rotatingdrum. Similarly, a separator material is configured to be pressed ontothe substrate over at least a portion of the ink using the rotarylithographic printer.

In some embodiments, a method of manufacturing an electrode includesprinting an electrode ink on a plurality of substantially similar shapedportions of a substrate such that the ink defines a pattern on thesubstrate. Each portion from the plurality of substantially similarshaped portions is mutually exclusive from the other portions from theplurality of substantially similar shaped portions. The electrode ink isallowed to dry on the substrate. A separator material is printed on topof at least one portion form the plurality of substantially similarshaped portions of the substrate.

Individual electrochemical cells have a finite voltage standoff due tothe electrolyte's breakdown limit, which is generally in the range of2.5-2.7 volts. In some embodiments, a manufacturing process allows anumber of individual half-cells to be produced on a substrate, which canbe folded with another substrate to produce a stack of low voltage cellsconnected in series. In some embodiments, such half-cells can bemanufactured by lithographically printing electrode ink in a matrix ofsubstantially similar shaped portions on the substrate. Similarly, asealant wall can be printed around the similar shaped portions and aseparator material can be printed on the electrode ink. The voltagestand off depends on the number of such cells within each stack andeliminates cell balancing issues.

In some embodiments, a single cell composite device is designed to use alarge number of individual cells in a single package, thus producing a“single cell” EDLC device with a higher voltage standoff than that ofconventional EDLCs. Such EDLCs can be lighter in weight, smaller involume, and inherently free of complications that arise from cellbalancing. The EDLC has a unit cell structure with alternatelyinterleaved electrodes formed lithographically and a preformed separatordisposed between the electrodes, also formed lithographically. Anelectrolyte is impregnated an within the EDLC. The electrodes can belithographically printed at precise intervals on a substrate referred toas a half-cell strip. On a first pass of the printing process an arrayof square or rectangular areas are defined and electrode ink is printedon the substrate. The printing process allows for varying the thicknessof the carbon layer and this influences the overall energy density ofthe half-cell strip. On a second pass a border of sealant material isformed, around each electrode. On a third pass a separator material isprinted on half of the half-cell strips. The strips are then joinedforming a completed EDLC cell. Extensions of individual stacks ofelectrodes are also provided, containing additive capacitance,interfaced by allowing extra lengths of current collector to one of theelectrodes and continuing forward with component placement or by sonicwelding or by heat (spot) welding the extension pieces together.

Some embodiments include manufacturing steps for a single high voltageEDLC cell. An example capacitance of 58 farads and a voltage standoff of15 volts is used hereinbelow. It is not intended that this example betaken as a standard; rather, it should be understood this is anarbitrary choice to illustrate the concept. The methodology way beextended to virtually any other capacitance and voltage stack.

FIG. 1 illustrates an electrode (e.g., a half-cell) throughout variousstages of the manufacturing process. Plan views of the manufacturingstages of the electrode are identified by reference numerals 10, 11, 12,13, 14 and 15, shown on the upper portion of FIG. 1, while therespective cross-sectional thickness of single and double layerelectrodes are identified by reference numerals 16, 17, 18, 19, 20, 21,22, and 24, shown on the lower portion of FIG. 1.

A current collector (e.g., a substrate) 10, 16 can be constructed of anysuitable material. For example, in some embodiments, the currentcollector 10, 16 is constructed of capacitor grade aluminum (e.g.,99.99% pure aluminum). In other embodiments, the current collector canbe constructed of tantalum and/of the like. The current collectors 10,16 can be available in sheets. In some embodiments, for example, a sheetcan have a thickness of 30 μm, a width of 50 mm and a length of 50 mm.In other embodiments, the sheets can be any suitable size. For example,in other embodiments the sheet can have a thickness of 40 μm. Thesubstrate material can be obtained in large rolls and can be slit toappropriate dimensions for the fabrication of a particular device. Insome embodiments, stationary knives are used to slit the substratematerial to the appropriate dimensions. Such stationary knives can beused to make a clean accurate cut that does not cause rolled edges onthe substrate. The process, as mentioned above, can be used forvirtually any size capacitor and the device capacitance is dependentupon the size of the half-cell structures, described in further detailherein.

In some embodiments, the current collector 10, 16 can be cleaned. Suchcleaning can help prevent the current collector from formingcontaminates that can reduce the strength of the bond between theelectrode material and the current collector 10, 16 when the electrodematerial is formed on the current collector 10, 16, as further describedin detail herein. For example, aluminum, when exposed to an oxygenatmosphere, can quickly form contaminates (e.g., aluminum oxide) thatcan impede the electrode material from bonding with an aluminum currentcollector. In some embodiments, plasma etching can be used to clean thecurrent collector 10, 16. In such embodiments, plasma etching can beused as part of a printing process, as described in further detailherein. As such, an apparatus (such, as apparatus 50 shown in FIG. 1A)can plasma etch, the current collector 10, 16 prior to printing theelectrode ink on the current collector 10, 16. In other embodiments,high voltage corona discharge cars be used to clean the currentcollector 10, 16. In still other embodiments, chemical etchant baths canbe used to remove such, contaminates. In such embodiments, the electrodematerial can be printed on the current, collector soon after the currentcollector is removed from the bath since an oxide layer can reform on analuminum current collector in a matter of minutes.

A hole 11 is formed in the current collector 10, 16. The hole 11 can beformed using any suitable technique. In some embodiments, for example,the hole 11 can be drilled, cut, and/or the like. The hole 11 can bealigned with the holes formed, in other current collectors. Anelectrolyte can be inserted, into a stack of cells via the holes, asdescribed in further detail herein.

A sealant material 12 is formed around the perimeter of the currentcollector 13. The sealant material 12 creates a sealant wall that willsurround the carbonized, material, as described in further detailherein. The sealant material 12 can be a polymer configured to adhere tothe sealant material on another current collector 13 to form ahermetically sealed barrier between the cell and the externalatmosphere. In such, a manner, two half-cells are combined to make afull cell. In some embodiments, a polyvinylidene fluoride (PVDF)material, such as, for example, Solef 1008 manufactured bySolvay-Solexis, can be used. Such a material can include desiredproperties such as operating temperature, surface adhesion, flexibility,and chemical solubility. In other embodiments, a CL-5-1 sealant materialcan be used. In some embodiments, the sealant material 12 can have athickness of less than 100 μm for a single side 19 and less than 170 μmfor a double sided component 20 (e.g., when the sealant material 12 isprinted on both sides of the current collector 13). The application ofthe sealant material can be through a lamination process, screenprinting and/or lithographic printing, as further described herein. Thesealant material 12 forms a wall around the perimeter of the currentcollector 13 that is immune to decay from electrolyte exposure andprevents leakage of electrolyte from the cell.

In some embodiments, the portion of the current collector on which thesealant material is formed can be perforated with micro holes such thatthe sealant material formed on a first surface of the current collectorcan be coupled with the sealant material formed on a second surface ofthe current collector. In such embodiments, for example, the sealantmaterial on the first surface or the current collector can bemonolithically formed and/or fused with the sealant material on thesecond surface of the current collector. This can help stabilize thewall created by the sealant material on both surfaces of the currentcollector.

An electrode ink is applied to the current collector 14. A side view 21of the current collector 14 having electrode ink applied on a singleside of the current collector 14 and a side view 22 of the currentcollector 14 having electrode ink applied to both sides of the currentcollector 14 are shown in FIG. 1. The electrode ink can be any suitableelectrode ink. In some embodiments, for example, the electrode ink canbe a carbon slurry similar to that described in U.S. patent applicationSer. No. 12/115,811, filed May 8, 2008, entitled “Electrode Structurefor the Manufacture of an Electric Double Layer Capacitor,” which isincorporated herein by reference in its entirety. The electrode ink canbe composed primarily of activated carbon (e.g., MSP-20), smallerquantities of conductive carbon (e.g., Super P), rubberizers (e.g.,BM-400-B), binders (e.g., polytetrafluoroethylene (PTFE),polyvinylpyrrolidone (PVP)), fillers (e.g., Cab-o-sil), distilled waterand/or other additives (e.g., carboxymethyl cellulose (CMC)). In someembodiments the electrode ink can be formed by mixing proper proportionsof the ingredients in specific a order, half mixing with itself and witha solvent. Once mixed, the electrode ink can be applied to the currentcollector (e.g., substrate). The electrode ink mixture has enhancedelectrical properties that reduce the bonding resistance and increasethe capacitance of the electrode ink promoting a unique east componentsolution. In other embodiments, the electrode ink can include ceramicsand/or the like.

Activated carbon, the predominant ingredient in an EDLC carbonelectrode, provides massive exposed surface areas used to create thecapacitive storage in high voltage EDLC applications. The capacitance ofa cell is proportional to the volume of the activated carbon within thecell. In some embodiments, a specific value can be obtained by takingthe product of the cell volume times the specific capacitance per unitvolume with the latter being relatively constant up to a moderatethickness. In other embodiments, the capacitance cars be obtained usingthe specific capacitance per unit area times the area of a cell. Asdiscussed in further detail herein, arranging multiple cells in seriesand parallel, can reduce the ESR of the electrode and thus increase thepower density of the electrode. Such an arrangement can also increasethe current carrying capability of the device.

Differing applications dictate the relative importance of power vs,energy density. The manufacturing process may be adjusted to prioritizeeither. In some embodiments, for example, the thickness of the electrodeink on the current collector and the adhesive thickness of the sealantmaterial on the current collector can be increased to increase theenergy provided by the cell. As further described in detail herein, thethickness of the electrode ink on the current collector can be varied bya thickness of a screen (e.g., a mesh) used in a lithographic printingprocess. As mentioned above controlling the thickness in turn changesthe energy density of the individual, half-cells.

In order to maximize the working voltage of the EDLC device, a protonconductor or separator 15 can be disposed between individual polarizedhalf-cells in order to electrically isolate but not chemically separatethe half-cells. The separator 15 can also be configured such that onlyspecific charged ions can pass through the separator 15. The separator15 can also store a limited amount of free electrolyte not absorbed intothe activated carbon. The separator 15 can be inserted or printed on oneof the half-cell strips using lithographic techniques, described infurther detail herein.

The separator 15 undergoes high mechanical stress, both in vertical andhorizontal directions, as the EDLC is charged and discharged inoperation. The separator 15 adds its own resistive quantities measuredas a constant in one direction or the opposite direction, and as somereactive component as a frequency dependent quantity. In someembodiments, a lithographic printing process can be used to print theseparator material onto the electrode ink, since precession location,material concentration, spacing, sizing and adaptability are importantparameters and may be more easily attained using a lithographic printingprocess.

In some embodiments, the separator 15 can be constructed of apolyvinylidene fluoride (PVDF), such as, for example, Solef 6020manufactured by Solvay-Solexis. In other embodiments, the separator canbe constructed of rubberizers (e.g., BM-440-B), binders (e.g.,polytetrafluoroethylene (PTFE), polyvinylpyrrolidone (PVP)), fillers(e.g., cab-o-sil), distilled water and/or other additives. In suchembodiments, the cab-o-sil forms a permeable membrane configured toallow electrolyte ions to pass through the separator material.

The separator 15 can be screen and/or lithographically printed onto theprepared, dried electrode ink, as described in further detail herein. Insome embodiments, for example, the separator 15 can have a maximumapplied thickness of 25 μm, a pore size of 25 to 50 μm with an evenlydistributed pore size distribution (PSD) and a homogenous separatormatrix composition. The pore size can dictate the rate of electrolytemigration in the cells. A small pour size, for example, can reduce therate of electrolyte migration in the cells which can slow the responseof the capacitor. Depending on the power or energy requirements of thefinal high voltage EDLC, the screening application process cancompensate for other material or manufactured defects. A single sidedelectrode 23 with a screened separator and a double-sided electrode 24(e.g., a half-cell printed on both surfaces of a current collector) withscreened separator are shown in FIG. 1. In some embodiments, theseparator can be as thin as possible to provide sufficient isolation, toprevent the two half-cells from shorting together. In some embodiments,only one separator 15 is required between each half-cell assembly, soalternate placement from the screening applicator may be possible.Accordingly, as described, in further detail herein, a separator 15 isnot printed on every current collector. After a completed, half-cell isprinted on a first surface of the current collector, a half-cell can beprinted on a second surface of the current collector using a similarprocess.

In other embodiments, the separator can be placed onto the prepared,dried electrode ink using methods other than printing. For example, apremade separator sheet can be placed and/or laminated onto the driedelectrode ink. Some separator materials used in such embodiments operatebest when formed prior to being placed onto the dry electrode ink. Suchmaterials are available from manufactures such as Celgard and NKK. Theoperation parameters of such separator materials can be predefined andtested by the manufacturer and as such, the materials can operate astested under various conditions. Such separators can be physicallyapplied to the current collector over the electrode ink the electrodesare manufactured or such separators can be laminated prior to assemblyof the electrode.

FIG. 1A is a schematic illustration of a rotary lithographic printer 50used to manufacture an electrode, such as the half-cells shown anddescribed in FIGS. 1B-1D, according to an embodiment. The rotarylithographic printer 50 includes a first pair of rotating drums 57, asecond pair of rotating drums 58 and a third pair of rotating drums 59.The first pair of rotating drums 57 includes a top drum 51 and a bottomdrum 52. The top drum 51 is a print head containing electrode ink. Insome embodiments, an outer mesh layer (not shown in FIG. 1A) is coupledto the top drum 51. The top drum is configured to press the electrodeink through the outer mesh layer and onto a current collector (e.g., asubstrate) when the current collector is passed between the top drum 51and the bottom drum 52.

The top drum 51 is configured to rotate about a center axis in thedirection, shown by the arrow AA in FIG. 1A. Similarly, the bottom drum52 is configured to rotate about a center axis in the direction shown bythe arrow BB in FIG. 1A. Accordingly, when a substrate is passed betweenthe top drum 51 and the bottom drum 52, the substrate is moved in adirection shown, by the arrow CC in FIG. 1A. This allows the top drum 51to print the electrode ink onto the substrate as the substrate is movedin the direction shown by the arrow CC.

In some embodiments, the top drum 51 prints the electrode ink in apattern across the substrate. In such embodiments, for example, the topdrum 51 can print an array of rectangles across a long strip ofsubstrate. Such an array of rectangles can be similar to those shown inFIGS. 1B-1D. In other embodiments, any other pattern can be printed,such as, for example, a pattern of triangles, circles, ovals and/or thelike.

In some embodiments, the top drum 51 prints the electrode ink in apattern across the substrate. In such embodiments, for example, the topdrum 51 can print an array of rectangles across a long strip ofsubstrate. Such an array of rectangles can be similar to those shown inFIGS. 1B-1D. In other embodiments, any other pattern can be printed,such as, for example, a pattern of triangles, circles, ovals and/or thelike.

The thickness of the electrode ink primed onto the substrate can bevaried by varying the outer mesh layer coupled to the top drum 51. Forexample, if a thicker layer of electrode ink is desired, the thicknessof the outer mesh layer can be increased. Further, if a thinner layer ofelectrode ink is desired, the thickness of the outer mesh layer can bedecreased. Varying the thickness of the electrode ink varies thecapacitance of the device. An optimal thickness of the electrode ink canbe determined by printing samples and measuring the capacitance per unitvolume of the samples, if the electrode ink is too thick, the electrodeink spaced far from the current collector does not function as intendedand can reduce the migration of electrolyte ions and thus the conductionrate across the separator layer. If the electrode ink is too thin, thecapacitance of the device can be less than the capacitance of anelectrode having electrode ink layer with optimal thickness.

Similar to the first pair of rotating drums 57, the second pair ofrotating drums 58 includes a top drum 53 and a bottom drum 54. The topdrum 53 is configured to rotate about a center axis in the directionshown by the arrow AA in FIG. 1A. Similarly, the bottom drum 54 isconfigured to rotate about a center axis in the direction shown by thearrow BB in FIG. 1A. Accordingly, when a substrate is passed between thetop drum 53 and the bottom drum 54, the substrate is moved in adirection shown by the arrow CC in FIG. 1A.

The top drum 53 is a print head containing separator material. In someembodiments, an outer mesh layer (not shown in FIG. 1A) is coupled tothe top drum 53. The top drum 33 is configured to press the separatormaterial through the outer mesh layer and onto a substrate on whichelectrode ink has been printed when the substrate is passed between thetop drum 53 and the bottom drum 54.

In some embodiments, the top drum 53 prints the separator material ontothe substrate in a pattern across the electrode ink. In suchembodiments, for example, the top drum 51 can print an array ofrectangular strips across a portion of a substrate on which electrodeink has been printed. Such an array of rectangular strips can be similarto those shown in FIGS. 1B and 1D. In other embodiments, any otherpattern can be printed.

As discussed above, in some embodiments, the separator material is notprinted on every current collector. For example, FIG. 1C shows a stripof substrate 1020 with half-cells 1030 on which separator material isnot printed. To achieve such a result, the top drum 53 can be configuredto print the separator material on some current collectors and notothers.

Similar to the first pair of rotating drums 57 and the second pair ofrotating drums 59, the third pair of rotating drums 59 includes a topdrum 55 and a bottom drum 56. The top drum 55 and the bottom drum 56 areconfigured to rotate similar to the top drum 51 and the bottom drum 52,described above. The top drum 55 is a print head containing sealantmaterial. In some embodiments, an outer mesh layer (not shown in FIG.1A) is coupled to the top drum 55. The top drum 55 is configured topress the sealant material through the outer mesh layer and onto asubstrate when the substrate is passed between the top drum 33 and thebottom drum 54. The sealant material can be printed such that sealantmaterial surrounds the portion of the substrate on which the electrodeink is printed.

In use, a piece of substrate material (e.g., aluminum) is inserted intothe apparatus 50 at point 60. Because of the rotational motion of therotating drum pairs 57, 58, 59, the substrate material is moved in thedirection shown by the arrow CC. As the substrate material passesthrough the first pair of rotating drums 57, the top rotating drum 51prints electrode ink on the substrate. As discussed above, in someembodiments, the top rotating drum 51 can print a pattern of electrodeink on the substrate, such as, for example, an array of rectangles.

The piece of substrate material then passes from the first pair ofrotating drums 57 to the second pair of rotating drums 58. The distancebetween the first pair of rotating drums 57 and the second pair ofrotating drums 58 can be large enough to allow the electrode ink printedon the substrate by the first pair of rotating drums 57 to dry on thesubstrate before the substrate reaches the second pair of rotating drums58. In other embodiments, the electrode ink need not be dried prior toprinting the separator material on the substrate. After the substratecontacts the second pair of rotating drums 58, the top rotating drum 53prints the separator material on the substrate in the desired patternand location. In some embodiments, for example, the separator materialis printed on only some of the half-cells. The piece of substratematerial then passes from the second pair of rotating drums 58 to thethird pair of rotating drums 59. The top rotating drum 55 prints thesealant material around the perimeters of the portions of the substrateon which the electrode ink was printed.

The printed substrate (e.g., completed half-cell strip) can then exitthe apparatus at point 62. The piece of substrate material can then beturned over and inserted through the apparatus 50 such that theelectrode ink, the sealant material and optionally, the separatormaterial is printed on a second surface of the substrate. Thepositioning of the components already primed on the first surface of thesubstrate (e.g., the electrode ink, the separator material and thesealant material) as the components are printed onto the second surfaceof the substrate can be monitored using optical sensors (not shown)positioned on the apparatus 50. Such optical sensors can help ensurethat the half-cells printed on the second surface of the substrate arealigned with the half-cells printed on the first surface of thesubstrate. In other embodiments, any other suitable method and/or deviceis used to monitor the positioning of the components already printed onthe first surface of the substrate as the components are printed ontothe second surface of the substrate. In still other embodiments,half-cells are printed on the second surface of the substrate by thebottom rotating drums as the top rotating drums print the half-cells onthe first surface of the substrate. In such embodiments, only a singlepass through the apparatus 50 is necessary to print half-cells on bothsides of the substrate.

In some embodiments, as each component (e.g., the electrode ink, theseparator material and the sealant material) is applied, drying time canfar modified (e.g., longer or shorter), as the substrate is wound onto alarge round dram that may be oil heated to maintain a satisfactorydrying temperature. The large drum may also be considered a storagevehicle to allow more substrate material in a smaller length of area andnot condensing it into a compact reel thus possibly damaging theintegrity of the sealant material and electrode ink.

While shown in FIG. 1A as printing the sealant material onto thesubstrate after printing the electrode ink and the separator onto thesubstrate, the sealant material can be printed onto the substrate at anypoint in the printing process. In some embodiments, for example, thesealant material is printed onto the substrate prior to printing theelectrode ink and the sealant material onto the substrate. In otherembodiments, the sealant material is printed onto the substrate afterprinting the electrode ink onto the substrate but prior to printing thesealant material onto the substrate.

While shown in FIG. 1A as having three rotating drum pairs 57, 58, 59,in other embodiments the apparatus can include a single rotating drumpair. In such embodiments, the top rotating drum can be reconfigured ateach stage of the printing process. For example, the top rotating drumcan first be configured to print the electrode ink on the substrate. Thesubstrate can then be passed between the rotating drum pair and theelectrode ink can be printed on the substrate. The top rotating drum canthen be reconfigured to print the separator material on the substrateand the substrate can be passed between the rotating drum pair a secondtime such that the separator material is printed on the substrate. Thetop rotating drum can then be reconfigured to print the sealant materialon the substrate and the substrate can be passed between the rotatingdrum pair a third time such that the sealant material is printed on thesubstrate.

FIGS. 1B-1D show examples of half-cell strips printed using theapparatus 50 of FIG. 1A. FIG. 1B, for example, shows a substrate 1000with four half-cells 1010 printed thereon. The electrode ink, theseparator material and the sealant material is printed on each of thefour half-cells 1010. FIG. 1C shows a substrate 1020 with fourhalf-cells 1030 printed thereon. The separator material is not printedon the four half-cells 1030 of substrate 1020. As described in furtherdetail herein, the substrate 1000 can be coupled with the substrate 1020to form multiple electrode cells connected in series.

While FIGS. 1B and 1C show a single row of half-cells printed on asubstrate, FIG. 1D shows a substrate 1040 having two rows of half-cells1050, 1060 printed thereon. The separator material is printed on somehalf-cells 1060 while not printed on other half-cells 1050. In someembodiments, the substrate 1040 can be folded to provide a seriesconnection between the electrodes in each row and a parallel connectionbetween the electrodes in the two rows. In other embodiments, any numberof rows and columns of any number of half-cells can be printed on thesubstrate. For example, FIG. 3 shows two substrates having fivehalf-cells each.

FIG. 1E is a flow chart illustrating a method 1070 of printinghalf-cells of an electrode on a substrate. The method includes cleaningthe substrate, at 1072. The substrate can be cleaned by, for example,plasma etching. Such cleaning can help prevent the current collectorfrom forming contaminates that can reduce the strength of the bondbetween the electrode material and the current collector when theelectrode material is printed on the correct collector.

An aperture formed in the substrate, at 1074. As discussed above, theaperture can be formed by any suitable method and electrolyte can beinserted into the aperture when the device is completed, as described infurther detail below. An electrode ink is printed onto a portion of thesubstrate using a rotary lithographic printer, at 1076. The electrodeink can include activated carbon and can be similar to the electrode inkshown and described above. Further, the rotary lithographic printer canbe similar to the apparatus 50 shown and described with relation to FIG.1A.

The electrode ink is allowed to dry on the substrate, at 1078. Aseparator material is printed onto the portion of the substrate usingthe rotary lithographic printer, at 1080. The separator material can besimilar to the separator material shown and described above. Moreover,the separator material can be printed onto the portion of the substratein a specific pattern, such as, for example, the checkered pattern shownon the half-cells 1010 of substrate 1000 in FIG. 1B. A sealant wall isprinted around the portion of the substrate using the rotarylithographic printer, at 1082. The sealant wall can be used tohermetically seal the half-cell with another half-cell to create acompleted full cell.

FIG. 2 details lithographic component plates, showing front 105, 110,115 and back 120, 125, 130 sides of a first substrate 100 and front 155,160 and back 165, 170 sides of a second substrate 150 at differentstages within the printing process. Each component of the printingprocess (e.g., the electrode ink, the separator material and the sealantmaterial) is sequentially applied onto the substrates 100, 150 until thecomponents are completed. The components can be applied to each side ofthe substrates 100, 150 as described above. As shown in FIG. 2, theseparator material is not applied to the second substrate 150.

Detailed information as to how the electrode components are assembledinto the high voltage EDLC are referenced initially by the sample 90degree lithographic component folding scheme shown in FIG. 3. A firsthalf-cell strip 280 comprises elements 115 and 130 (FIG. 2) and a secondhalf-cell strip 290 comprises elements 160 and 170 (FIG. 2) arranged 90degrees offset from each other 200, both half-cell strips 280, 290having the respective front sides facing up. A separator material isprinted on the half-cells of the first half-cell strip 280 while aseparator material is not printed on the half-cells of the secondhalf-cell strip 290. As the half-cells of the first half-cell strip 280are coupled to the half-cells of the second half-cell strip 290, eachfull cell will have a separator material between the electrode ink.

The folding pattern demonstrates how individual components are aligned.Beginning with folding pattern 200 of half-cell strip 280, the firstbottom component 201 has bare aluminum ready for block assembly,described in further detail herein. Initially half-cell strip 290 slidesdown on top of half-cell strip 280 forming the first full cellcomponent. The half-cell strip 290 is then folded over the half-cellstrip 280 in the direction shown by the arrow 206, at 205. This foldforms a second full cell component. The half-cell strip 290 is thenfolded over the half-cell strip 280 in the direction shown by the arrow211, at 210. This fold forms a third full cell component. This foldingprocess is repeated at steps 215, 220, 225, 230 and 235 until the lastfolding pattern 240, folds the half-cell strip 290 over the half-cellstrip 280 in the direction shown by the arrow 241 and the operation iscomplete with the top end component 245 of half-cell strip 290 on top ofthe additive capacitive block. Such a folding process produces a slackof multiple full cells connected to each other in series. For example,in FIG. 3, the folding process results in a stack of nine full cellsconnected in series.

As each of these electrode assemblies is built, it is targeted forspecific sections, being defined as block and block interface couplingareas. The most straight forward is the block area. In this area, thetwo electrodes are intertwined, coupling the carbon-to-carbon interfacetogether with only one thin separator sandwiched between them. As eachelectrode is advanced, it is folded 90 degrees to the second electrodewith each electrode being placed down in series to the other. Everysecond time an electrode is placed down, an additive capacitivecomponent is created. As long as each electrode is interfacing in thisseries fashion with continuous lengths of current collector matching,the capacitance is additive.

At the beginning of the electrode, a carbon mass-free aluminum currentcollector component is provided (e.g., bottom component 201 in FIG. 3).This also occurs at the very end of the completed EDLC block (e.g.,component 245 in FIG. 3). These bare aluminum segments, at least on oneside, when the EDLC is first connected to a positive and negative powersource, act as the terminal interface.

A stack produced by the folding process 200 of FIG. 3 can be coupled toother similar stacks in parallel. For example, FIG. 3A shows four stacks255 coupled to each other in parallel by a conductor 260 (e.g., a pieceof aluminum). Specifically, the conductor 260 is coupled to the top barecomponent (e.g., component 245 in FIG. 3) of each of the stacks 255.Similarly, the bottom bare component (e.g., component 201) of each ofthe four stacks 255 is coupled to the bottom bare component of the otherstacks by a conductor (not shown in FIG. 3A). Such a series/parallelconfiguration (e.g., cells coupled in series within each stack and cellscoupled in parallel between each stack) can increase the power densityof the device. Such configurations reduce the ESR and thus increase thepower density and provide a device having a more robust current carryingcapability than a single stack of cells.

Depending on the structural size and organization of these componentareas, orienting length, width and thickness in parallel and/or seriescompartments provides greater capacitance and/or voltage standoffcapability, respectively. To illustrate suppose multiple half-cellstrips have been joined forming an EDLC device with n individual cellsin series (e.g., the number of ceils in each stack 255) and m in stacksin parallel (e.g., the number of stacks 255). The capacitance of eachstack can be equal to the capacitance of each cell divided by the numberof cells in each stack (C_(stack)=C_(cell)/n). The voltage standoff ofeach stack can be equal to 2.5 times the number of cells in each stack(V_(standoff)=2.5×n). The capacitance of the device can be equal to thenumber of stacks times the capacitance of each cell divided by thenumber of cells in each stack (C_(total)=(m×C_(cell))/n). The ESR ofsuch a device can be the ESR of each stack divided by the number ofstacks (ESR_(total)=ESR_(strip)/m).

FIG. 4 shows a single electrode capacitive segment folding view 300,indicating layer detail. One side of the segment is free from materialincluding components 305 or both sides, depending on the application anddesired termination method. Considering only one electrode side exposed,the other side may have components consisting of carbon mixture only oran additional component such as the separator.

FIG. 5 shows a device 400 having three stacks of cells 405, 406, 407coupled together in series. This can be done to increase the voltagestandoff of the device 400. In some embodiments, a stack-to-stackinterface 415 can be used to couple a first stack of cells 405 to asecond stack of cells 406. In coupling the first stack 405 to the secondstack 406, the stack-to-stack interface 415 can be coupled to anelectrode other than the outermost bare electrode (e.g., component 245in FIG. 3). For example, the stack-to-stack interface 415 can be coupledto the second electrode in the first stack 405 rather than the outermostbare electrode.

The stack-to-stack interface 415 is coupled to the second stack 406,electrically coupling the first stack 405 with the second stack 406. Thestack-to-stack interface 415 can be coupled to the outermost bareelectrode of the second stack 406 or the second electrode in the secondstack 406. The stack-to-stack interface 415 can be coupled to the firststack 405 and the second stack. 406 by any suitable method, such asultrasonic welding or the like. The resulting concatenated linkage(s)enable the voltage dividing necessary to be able to stack up to thecomplete EDLC voltage requirement.

An aperture 410 is defined by each component area, whether or not thecomponent includes separator material. These apertures 410 allow anelectrolyte to be filled throughout the enclosed cavity, to permeate theporous activated carbon, and saturate the separator. Since theseapertures 410 are thru-connected per stack of cells only and each stackremains at its own potential, the apertures 410 can be plugged after theelectrolyte is inserted into the apertures 410. In order to ensure acomplete fill and to keep the oxygen level as low as possible, the stackcan be first evacuated and back filled, replacing the vacuum withnitrogen such that air contaminates do not linger, forming a prematurebreakdown in the electrolyte when refilled. Once the nitrogen hassaturated the carbon and separator material, the process is reversed,allowing the electrolyte to replace the nitrogen. Sealing can beprovided with Solef 1008, formed into a slug and injected into the stackthrough the holes. As the plug is injected it can be heated first toexpand the material entering into the cavity and then cooled to providea smooth thin outline on the exterior of the cavity.

A stack can include as many cell components as needed to obtain thedesired capacitance. The stack-to-stack interface between slacks can bekept as short as possible. In some embodiments, the stack-to-stackinterface between the slacks can be no more than one component inlength. There can be as many stack-to-stack interfaces us needed tosupply the voltage standoff required for a particular application.

The resultant cascading of stacks attached into one series stack can beseen in FIG. 6. In one embodiment, for example, the complete inventionexample assembly 500 can have a capacitance of 58 farads rated at 15volts. In other embodiments, any capacitance rated at any voltage can beobtained by varying the properties of each cell, the number of cells ina stack, and the number of stacks connected in series. Additionally, asdescribed above, the capacitance and voltage rating can be varied byconnecting multiple stacks in parallel. FIG. 6 shows six stacks 505,510, 515, 520, 525, 530 having equal capacitance and structure coupledto each other in series. The total voltage 540 can be determined by thenumber of stacks within the structure and the electrolyte. In someembodiments, the electrolyte can be, for example, TEABF₄/acetonitrile orTEABF4/propylene carbonate and/or TEMABF4/acetonitrile orTEABF₄/propylene carbonate. In some embodiments, each stack 505, 510,515, 520, 525, 530 can have a voltage rating of 2.7 or 2.5 volts whenthe above electrolytes are used.

In some embodiments, the electrode 590 can be 50 mm in width 592 and 50mm in height 594. In other embodiments, the electrode can have any othersuitable width and/or height. Its some embodiments, the sealant material596, 598 printed on the perimeter of each electrode can be less than 5mm wide. In other embodiments, the sealant material can have a widthgreater than 5 mm. In some embodiments, the electrode 590 can beapproximately 162 μm wide, including electrode ink printed on both sidesof the current collector. Measuring the surface area using the techniquedisclosed in the co-pending patent application Ser. No. 12/151,811,activated carbon mix and the amount of material used, the specificcapacitance can be determined. From the above information the calculatedcapacitance equals the working volume of the electrodes multiplied bythe specific capacitance of a single electrode assembly. In the 58farad, 15 V assembly, for example, the calculated capacitance can beapproximately 10.14 farads.

An electrode assembly 600 shows the individual layers and the actualsequence of placement. A first electrode 605, 610, 615, on whichelectrode ink has been printed on both surfaces, is disposed on top ofan aluminum current collector 610, adjacent to a separator 620. A secondelectrode 625, 630, 635, on which electrode ink has been printed on bothsurfaces, is disposed on top of an aluminum current collector 630. Inthe 58 farad, 15 V assembly, for example, the nominal thicknesses605-635 can be obtained and summarized, having a total electrodeassembly thickness result 640 of 357 μm or 0.357 mm.

The stack or voltage segment 550 shows the 35 components of eachelectrode or the 70 total half-cells that can be used in a 350 faradstack assembly, in some embodiments. In such an example, the totalresulting thickness of the stack 585 can be 12.6 mm. Each end of thestack, has stack-to-stack interface 560, 575 (FIG. 6). Such astack-to-stack interface 560, 575 can be structurally and functionallysimilar to the stack-to-stack interfaces 415, 420 shown and described inFIG. 5. Each stack end has a different electrode polarity extending out,thereby forming the series connectivity.

The aperture defined in each electrode is aligned with the aperturesdefined in the other electrodes 555, 580 (FIG. 6). As described above,electrolyte can be inserted into the device through the apertures. Insome embodiments, after an individual block has been filled withelectrolyte, the holes are plugged with a PVDF homopolymer and sealed,leaving a uniform finish on the surface. Each block section is similarlyfilled with electrolyte until the total stack is completed. Since eachblock is mechanically and electrically temporarily fitted, preliminarytests for acceptance, such as capacitance and voltage withstanding, canbe measured at this stage of manufacture. FIG. 7 shows a semifinal viewof the complete example high voltage stack 700. The extended electricalend current collector components, negative 710 and positive 715,stack-to-stack interfaces 705 and capacitive stack sections 720, 725,730, 735, 740, 745 are shown in exploded detail.

In some embodiments, a high voltage stack 700 having multiple stacksections 720, 725, 730, 735, 740, 745 (e.g., multiple unit cells)coupled together in series can be coupled in parallel to one or moreother high voltage stacks. This can be similar to the parallelconnection, shown and described with respect to FIG. 3A.

If some embodiments, an efficient thermal heat transfer mechanism can beused to remove internally heated mass to an exterior, coolerenvironment. For example, as the high voltage EDLC operates, continuedpower cycling generates unwanted heat within the structure. FIG. 8 showsa device 800 having three stacks of electrodes 815 coupled together viatwo stack-to-stack interfaces 820. A transfer material 825 can beinserted at the intersections of the stack-to-stack interfaces 820. Insome embodiments, the transfer material 825 can be a thin porous andthermally efficient conductive transfer material, such as a conductiveepoxy and/or the like. In some embodiments, the transfer material can beprefabricated to help direct and dissipate unwanted heat. In someembodiments, the transfer material 825 can be added when an applicationrequires either continual power cycling or a high level of deep drawnvoltage surges requiring large masses of charged ionic particles tomigrate between the EDLC's double layers. Additionally, the 90 degreeoffset folding scheme described in FIG. 3 and the two exposed edges 710,715 shown in FIG. 7, create a unique natural thermal dissipater. Theseexposed aluminum side ended areas conduct internally generated heat intothe containment shell shown in FIG. 9.

FIG. 9 shows a complete stack 900 compressed into its final form and acomplete stack 920 disposed within the final package 915. The aluminumcurrent collector components that remain on the left and right sides forterminal connection are connected by sonic or electrical spot welding topreformed terminal plates and/or pole pieces. As can be seen in FIG. 9,the complete stack 900 includes welded pole pieces 905. These polepieces are part of the final package 915 and are constructed to allow ahigh density polyethylene (HDPE) to be formed around the peripheralsurface to ensure an airtight seal of the final package 915. Aluminum orstainless steel pole pieces 905 are used to solidify the ends into afinal package 915, allowing the EDLC components to electrically gainaccess through the packaging. The solid pole pieces 905 help commute theinternal heat buildup from the inside to the outside of the package.

Since other modifications and changes varied to fit particular operatingrequirements and environments will be apparent to those skilled in theart, the invention is not considered limited to the examples chosen forpurposes of disclosure, and covers all changes and modifications whichdo not constitute departures from the true spirit and scope of thisinvention.

While methods and apparatus are shown and described above as printingand assembling electrodes for EDLCs, in other embodiments, such methodsand apparatus can be used to print and/or assemble electrodes forpseudocapacitors, batteries and/or any other device having an electrode.For example, pseudocapacitors have a similar structure andcharacteristics to EDLCs and can thus, be manufactured using the abovedescribed methods. Pseudocapacitors include cells with one electrodehaving metal oxide as the active material and the other electrode havingactivated carbon as the active material. The metal oxide can be printedonto a substrate using the methods and apparatus described above. Themetal oxide electrode of a pseudocapacitor stores energy using a faradicreaction on the electrode surface (e.g., similar to battery technology)in addition to using surface area storage similar to EDLCs. Accordingly,in some embodiments, a pseudocapacitor can have a higher energy densitythan a similarly sized EDLC. Moreover, in some embodiments, the load ofthe metal oxide of a pseudocapacitor is three times the load of an EDLChaving similar sized printed electrodes. Accordingly, pseudocapacitorcells can occupy a much smaller volume than an EDLC with the samecapacitance.

While various embodiments have been described above, it should beunderstood that they have been presented by way of example only, and notlimitation. Where methods described above indicate certain eventsoccurring in certain order, the ordering of certain events may bemodified. Additionally, certain of the events can be performedconcurrently in a parallel process when possible, as well as performedsequentially as described above.

Although various embodiments have been described as having particularfeatures and/or combinations of components, other embodiments arepossible having a combination of any features and/or components from anyof embodiments where appropriate. For example, each stack of electrodescan include any number of cells.

What is claimed is:
 1. A method of manufacturing an electrode,comprising: printing an electrode ink on a plurality of substantiallysimilar shaped portions of a substrate such that the ink defines apattern on the substrate, each portion from the plurality ofsubstantially similar shaped portions being mutually exclusive from theother portions from the plurality of substantially similar shapedportions; allowing the electrode ink to dry on the substrate; andprinting a separator material on top of at least one portion from theplurality of substantially similar shaped portions of the substrate. 2.The method of claim 1, wherein the printing the electrode ink on theplurality of substantially similar shaped portions of the substrateincludes printing the electrode ink on a plurality of rectangular shapedportions of the substrate such that the each rectangular portion fromthe plurality of rectangular portions is substantially aligned with theother rectangular portions from the plurality of rectangular portions.3. The method of claim 1, wherein the printing the electrode ink on theplurality of substantially similar shaped portions of the substrateincludes printing the electrode ink on a plurality of rectangular shapedportions of the substrate, each rectangular shaped portion from theplurality of rectangular shaped portions being spaced a distance from atleast one other rectangular shaped portion from the plurality ofrectangular shaped portions.
 4. The method of claim 1, wherein theprinting the electrode ink on the plurality of substantially similarshaped portions of the substrate includes printing the electrode inkusing a rotary lithographic printer having a first rotating drum and asecond rotating drum, the first rotating drum pressing the electrode inkthrough a mesh and onto the substrate as the substrate passes betweenthe first rotating drum and the second rotating drum.
 5. The method ofclaim 1, wherein the printing the electrode ink on the plurality ofsubstantially similar shaped portions of the substrate includes printingthe electrode ink using a rotary lithographic printer having a firstrotating drum and a second rotating drum, the first rotating drumpressing the electrode ink through a mesh and onto the substrate as thesubstrate passes between the first rotating drum and the second rotatingdrum, an amount of electrode ink applied to the substrate being variedwith a thickness of the mesh.
 6. The method of claim 1, wherein thesubstrate is aluminum.
 7. The method of claim 1, further comprising:printing a sealant wall around each portion from the plurality ofsubstantially similar shaped portions.
 8. The method of claim 1, whereinthe substrate is a first substrate and the electrode ink is a firstelectrode ink, the method further comprising: printing a secondelectrode ink on a plurality of substantially similar shaped portions ofa second substrate; allowing the second electrode ink to dry on thesecond substrate; and coupling a portion from the plurality ofsubstantially similar shaped portions of the second substrate with theat least one portion of the first substrate such that the secondelectrode ink contacts the separator material.
 9. The method of claim 1,wherein the separator material is printed on top of the electrode inkusing a rotary lithographic printer having a first rotating drum and asecond rotating drum, the first rotating drum pressing the separatormaterial through a mesh and onto the electrode ink as the substratepasses between the first rotating drum and the second rotating drum, anamount of separator material applied to the electrode ink being variedwith a thickness of the mesh.
 10. The method of claim 1, furthercomprising: cutting the substrate to a desired size.
 11. The method ofclaim 1, wherein the electrode ink includes activated carbon being inelectrical connection with the substrate when disposed on the substrate.